KingCoat SF100®
Two-component, solvent-free high build epoxy protective coating.
Overview
KingCoat SF100 is a solvent free, high build, epoxy protective coating based on specially formulated, pigmented epoxy/ hardener system. KingCoat SF100 is formulated to provide excellent impact, penetration and abrasion resistance along with excellent adhesion, flexural and tensile strength. The full compatibility with cathodic protection systems is a major advantage of the product. KingCoat SF100 is sprayable with standard or plural component heavy-duty airless spray machines. It can also be supplied in other grades like brushing grade, or rapid curing grade sprayable with twin component hot airless spray machines. KingCoat SF100 is supplied as a two-component product in pre-weighed base and hardener packs, ready for site
Applications
- Self-priming for vessel interiors, tanks, and piping (buried or exposed)
- Lining of storage tanks and silos
- Concrete and steel coating for chemical and pharmaceutical industries, sewage works, farms, agricultural firms, etc
- Pigmented flooring material for car parks, roads, airfields, traffic activities, industrial plants, and commercial warehouses
- Concrete topping for health care facilities, and food, beverage, and power plant industries
- Highly recommended in chemical and food industries with severe corrosion and abrasion environments
Advantages
- Solvent free Abrasion and wear resistant
- Easy to clean
- Full compatibility with cathodic protection systems
- Excellent resistance to a wide range of chemicals and solvents
- Excellent resistance to petroleum products such as gasoline, kerosene, naphtha, diesel, and fuel oil
- Excellent resistance to immersion in both fresh and salt water
- Excellent concrete protection
- the correct quantity of KingMix to the concrete mix
- coating
Technical Properties
| Property | Value | Standard |
|---|---|---|
| Mixing ratio | 2:1 (by volume) | — |
| Volume of solids | 100% | — |
| Pot life | 40 min @ 5oC 25 min @ 23oC 10 min @ 35oC | — |
| Touch dry | 8 hr @ 5oC 2 hrs 15 min @ 23oC 1 hr @ 35oC | — |
| Over coating time | 48 hr @ 5oC 24 hr @ 23oC 24 hr @ 35oC | — |
| Foot traffic | After 5 h | — |
| Service Temperature | -15 to 100oC -10 to 90oC Intermittently Continuously | — |
| Compressive strength | ISO ≥ 60 MPa @ 7 days 604 | — |
| Flexural strength | ≥ 30 MPa @ 7 days | — |
| Tensile strength | ≥ 20 MPa @ 7 days | — |
| Taber abrasion resistance | 600 milligram (1000 g, 1000 cycle) , weight loss H22 wheel | ASTM D968 |
| Shore D Hardness | ≈ 86 Adhesion strength on blasted ≥ 30 MPa | — |
| steel | Bond strength over C25/30 Concrete failure | ASTM D4541-2 |
| concrete | ASTM D4541 | |
| Izod impact, notched | ASTM 0.64 ft.lb./in D256 | — |
| Carbamation test | (scale 1 -5, 5 5 being best) | — |
Standards & Approvals
Usage & Packaging
KingCoat SF100 is available in: 56.7 litre set (three individual buckets of 18.9 litre), with a volume mixing ratio of 2:1 567 litre set (three individual buckets of 189 litre), with a volume mixing ratio of 2:1 Other mixing ratios are available upon requ
Approximately 0.5 – 2.0 ltr/m² to achieve thickness of 500– 2000 microns. Note: KingCoat SF100 can be applied at higher or lower thickness if needed.
Shelf life is 1 year when stored under cover, out of direct sunlight and protected from extremes of temperature
Bucket
Product family
High performance flexible epoxy polyurethane resin protective coating.
One component water based acrylic elastomeric protective anti carbonati…
Water based high performance acrylic protective and decorative coating.
Water based high performance acrylic protective and decorative coating …