KingRep 60T®
One component high build high strength cementitious repair mortar.
Overview
KingRep 60T is a one component polymer modified and fibre reinforced repair mortar. KingRep 60T is a blend of dry powders, selected aggregates and fibres which when mixed with water produces a thixotropic mortar suitable for vertical and overhead application.
Applications
- Repair of all types of structural concrete where high strength and extremely low shrinkage properties are required
- For the repair of vertical and overhead elements
- As a repair mortar for all structural elements in buildings, water retaining structures, industrial plants, bridges, etc
Advantages
- Shrinkage controlled polymer modified cementitious repair mortar
- Easy to apply, single component, requires only addition of water
- Extremely low permeability to water, providing excellent protection to steel reinforcements and host concrete
- Thixotropic properties allowing extra high build for vertical and overhead applications
- Suitable for internal and external application
- Water vapour permeable
- Suitable for use in contact with potable water
- Cost effective, hand applied no formwork is required
- STANDARDS KingRep 60T complies with the requirement of EN 1504-3 as structural repair mortar of Class R4
- KingRep 60T complies with the requirements of BS 6920 for the suitability of the product for use in contact with water intended for human consumption
Technical Properties
| Property | Value | Standard |
|---|---|---|
| Colour | Grey & white | — |
| Fresh wet density | 2.1 ± 0.1 g/cm³ | — |
| Minimum application | 5°C | — |
| temperature | — | |
| Compressive strength | ASTM ≥ 60 MPa @ 28 days C109/109M | — |
| Flexural strength | ASTM: ≥ 10 MPa @ 28 days C348 | — |
| Tensile strength | ≥ 3 MPa @ 28 days | ASTM C307 |
| Change in length | ASTM: Up to 0.1% @ 56 days C157 | — |
| VOC | : ≤ 5 g/ltr | ASTM D2369 |
| Performance | Measured | EN 1504-3 |
| characteristics | Requirement for Value Class R4 | — |
| Compressive strength | ≥ 45 MPa: ≥ 55 MPa | EN 12190 |
| Chloride content | EN ≤ 0.05%: 0.01% 1015-17 | — |
| Adhesive bond | EN: ≥ 2 MPa ≥ 2.25 MPa 1542 | — |
| Carbonation | ≤ control concrete Passes | — |
| resistance | MC (0,45) Thermal compatibility ≥ 2 MPa | EN 13295 |
| freeze-thaw | EN 13687-1 | |
| Dangerous substance | Complies with 5.4 | — |
| Note | Declared results above are for the grey colour. Remove all concrete form around exposed steel reinforcements by 10 mm thickness. The perimeters of the repair area should be saw cut to a minimum depth of 10 mm. The prepared area should be cleaned thoroughly by brush and/or compressed air. The prepared area should be cleaned thoroughly by brush and/or compressed air. | — |
Standards & Approvals
Usage & Packaging
KingRep 60T is available in 25 kg bags. KingRep 60T can be applied in a single application for sections up to 50 mm thick in overhead applications and 75 mm thick in vertical applications. Thickness should not be less than 10 mm deep in all applications.
Approximately 13.5 - 14 litre per 25 kg bag. (76 bags/m³).
Shelf life is 1 year when stored under cover, out of direct sunlight and protected from extremes of temperature
Bag, Can
Product family
Crack filling polymer modified cementitious fairing coat repair mortar.
Shrinkage compensated free flowing micro concrete.
Medium build, high strength cementitious repair mortar.
One component medium build cementitious repair mortar.