KingRep 100LE®
Medium build, high strength cementitious repair mortar.
Overview
KingRep 100LE is a single component polymer modified cementitious repair mortar consists of a blend of cement, dry powders, well graded aggregate and special additives that when mixed with water produces an easily workable repair mortar for horizontal and vertical applications.
Applications
- Repair of all types of structural concrete where high strength and extremely low shrinkage properties are required
- For the repair of vertical and overhead elements
- As a repair mortar for all structural elements in buildings, water retaining structures, industrial plants, bridges, etc
Advantages
- Shrinkage controlled polymer modified cementitious repair mortar
- Easy to apply, single component, requires only addition of water
- Extremely low permeability to water, providing excellent protection to steel reinforcements and host concrete
- Suitable for internal and external application
- Water vapour permeable
- Cost effective, hand applied no formwork is required
Technical Properties
| Property | Value | Standard |
|---|---|---|
| Colour | Grey | — |
| Density | 2.2 ± 0.1 g/cm3 | — |
| Compressive strength | ASTM ≥ 50 MPa @ 7 days ≥ 58 | — |
| C109/109M-02 | MPa @ 28 days | — |
| Flexural strength | ASTM: ≥ 6 MPa @ 28 days C348 | — |
| Minimum application | 5°C | — |
| temperature | — |
Usage & Packaging
KingRep 100LE is available in 25 kg bags. KingRep 100LE can be applied in a single application for sections up to 20 mm thick in overhead applications and 30 mm thick in vertical applications. Thickness should not be less than 10 mm deep in all applicatio
Approximately 13 litre per 25 kg bag. (77 bags/m3).
Shelf life is 1 year when stored under cover, out of direct sunlight and protected from extremes of temperature
Bag, Can
Product family
Crack filling polymer modified cementitious fairing coat repair mortar.
Shrinkage compensated free flowing micro concrete.
One component medium build cementitious repair mortar.
Two component polymer modified cementitious fairing coat and cosmetic r…