Concrete Repair & Strengthening Systems
KingRep 5E®
One component polymer modified cementitious fairing coat and cosmetic repair mortar.
Fresh wet density
1.75 ± 0.10 g/cm³
Maximum aggregate size
0.1 mm
Application thickness
Up to 3 mm
PROPERTY
EN 1504-3 MEASURED
EN 1504-3
Coverage
19 litre per 25 kg …
Packaging
Bag
Overview
KingRep 5E is a one component acrylic polymer modified powder. When mixed with water KingRep 5E produces a highly consistent, smooth, fine, trowel able mortar.
Applications
- For fair face concrete repair
- As a thin layer render
- As a skim coat for pin holes and minor honeycombed concrete repair
- As pore sealer and leveling mortar
- To produce a uniform surface for subsequent paint finish
Advantages
- Shrinkage controlled polymer modified cementitious repair mortar which reduces any potential cracking
- Easy to apply, single component which requires only addition of water
- Excellent adhesion to concrete, no independent primer or curing is required
- Compatible with other types of protective coatings
- Can be applied to feather edge thicknesses
- Suitable for internal and external applications
- Cost effective, hand applied no formwork is required
- STANDARDS KingRep 5E complies with the requirement of EN 1504-3 as non-structural repair mortar of class R2
Technical Properties
| Property | Value | Standard |
|---|---|---|
| Colour | Grey & white | — |
| Fresh wet density | 1.75 ± 0.10 g/cm³ | — |
| Maximum aggregate size | 0.1 mm | — |
| Application temperature | 5 - 35oC | — |
| Application thickness | Up to 3 mm | — |
| Flexural strength | ASTM: ≥ 3 MPa @ 28 days C348 | — |
| Tensile strength | ≥ 1.2 MPa @ 28 days | BS 6319-7 |
| VOC | : ≤ 10 g/ltr | ASTM D2369 |
| PROPERTY | MEASURED | EN 1504-3 |
| REQUIREMENT | VALUE FOR CLASS R2 | — |
| Compressive | ≥ 15 MPa ≥ 18 MPa | — |
| strength | EN 12190 | |
| Adhesion bond | ≥ 0.8 MPa ≥ 1.5 MPa | EN 1542 |
| Thermal | ≥ 0.8 MPa ≥ 1.0 MPa compatibility | — |
| freeze/ thaw | EN 13687-1 | |
| Chloride ion | ≤ 0.05% 0.015% | — |
| content | EN 1015-17 | |
| Dangers | Complies with | — |
| substance | 5.4 For one full bag, 7.5 - 8.5 litre of fresh water should be added to a clean container. The powder is then added slowly to the water while mixing continuously with low speed mixer/drill (400 - 600 rpm). Mixing time should be continued for 3 minutes until uniform consistency is obtained. To enhance the scratch resistance of KingRep 5E, an addition of KingBond SBR is advisable. 50% of the total mixing water shall be replaced by KingBond SBR range. PLACING AND FINISHING KingRep 5E can be applied by steel trowel. The mixed mortar can be applied to the prepared substrates at up to 3 mm thicknesses. The applied mortar should be allowed to stiffen before trowelling to a smoother finish. KingRep® 5E One component polymer modified cementitious fairing | — |
Standards & Approvals
ASTM
ASTM D2369
BS
BS 6319-7
EN
EN 1015-17
EN
EN 12190
EN
EN 13687-1
EN
EN 1504-3
EN
EN 1542
ISO
ISO 9001 · 14001 · 45001Quality & EHS
Usage & Packaging
Packaging
KingRep 5E is available in 25 kg bags.
Coverage
Approximately 19 litre per 25 kg bag.
Storage
Shelf life is 1 year when stored under cover, out of direct sunlight and protected from extremes of temperature
Pack formats
Bag
Product family
Part of the KingRep range
KingRep 10
Crack filling polymer modified cementitious fairing coat repair mortar.
View product →
KingRep 100HFShrinkage compensated free flowing micro concrete.
View product →
KingRep 100LEMedium build, high strength cementitious repair mortar.
View product →
KingRep 100LSOne component medium build cementitious repair mortar.
View product →