KingFloor C200SL®
Cement based self-leveling industrial surface system.
Overview
KingFloor C200SL is designed as an industrial grade floor topping for upgrading and renovating new and existing internal floors. KingFloor C200SL is supplied as a pre-blended dry powder designed for application between 5 mm to 50 mm (in one application) to provide a finished sound floor.
Applications
- It is suitable for use in a wide range of industrial environments such as Warehouses, food processing plants, industrial floors, car parks, etc
- Pour or pump the mixed material onto the prepared surface and allow to attain a smooth finish. The use of a spiked roller will help eliminate entrapped air and smooth out flow lines. Apply at a thickness between of 5 - 50 mm in one pass
- It is always better to work in manageable sections of approximately 20 m². It is recommended to seal KingFloor C200SL with suitable epoxy resin or solvent based resin sealer, especially if water may come into direct contact with the cured KingFloor C200SL. Where materials are to be applied over the surface of the hardened KingFloor C200SL, it is good practice to SHOT BLASTING the surface prior to carrying out subsequent treatments
Advantages
- Self-smoothing
- Dimensionally stable
- Fast drying
- Can be applied by pump
- KingFloor C200SL can be pumped to cover an area of 2000 m2 per day. Alternatively a coverage of 600m2 per day can be achieved when hand applied, depending on manpower, thickness applied and equipment used
- STANDARDS KingFloor C200SL complies with EN 13813, Class CT- C35- F5-AR1
Technical Properties
| Property | Value | Standard |
|---|---|---|
| Flow properties using 35 cc Initial ≥ 120 mm After 15 | ||
| flow ring | : min ≥ 110 mm | ISO 554 |
| Workability | 15 - 20 min | — |
| Vicat setting time | 2 hr | — |
| Foot traffic | Light traffic: 24 hr 48 hr | — |
| *Compressive strength | > 25 MPa @ 7 days > 35 /109M-02 BS EN MPa @ 28 days 13892-2 | ASTM C109 |
| Flexural strength | , > 5 MPa @ 7 days > 7 | BS 6319 |
| Part 3 | 1990 MPa @ 28 days > 5 MPa @ 28 days | BS EN 13892-2 |
| Maximum wear depth | BS EN 0.1 mm 13892-4 | — |
| Maximum application | 35oC | — |
| surrounding temperature | — | |
| Maximum mixed material | 32oC | — |
| temperature | — | |
| Shrinkage (μ/m) | ASTM: < 400 @ 28 days C490-00a | — |
| Application thickness | 5 – 50 mm | — |
| Bond strength to concrete | > 1.5 MPa @ 28 days | ASTM C1583 |
| VOC | : < 5 g/ltr | ASTM D2369 |
| *Note | dry cure for compressive and flexural strengths. Concrete surfaces are to be mechanically prepared to remove laitance and achieve a flat surface, grit blasting or surface profiling equipment are preferred. Acid etching can be used after consulting with KINGKRETE's Technical Department. Surface defects such as voids and blowholes should be repaired before application. Consult KINGKRETE's Technical Department for the best repair material. Surfaces must be free of any dust or loose particles before product application. Use suitable methods like vacuuming or sweeping. If possible, apply the product on a small test area before actual application to check for any problems with the | — |
Standards & Approvals
Usage & Packaging
KingFloor C200SL is available in 25 kg bags. Cemflow Acrylic Primer is available in 5 and 25 litre pails.
KingFloor C200SL: 1.36 m2 @ 10 mm thickness for 25 kg bag mixed with 4.5 litre of clean water. KingFloor Acrylic Primer when diluted 3 parts potable water to one part primer: 30 m2/5 litre. 150 m2/25 litre.
Shelf life is 1 year when stored under cover, out of direct sunlight and protected from extremes of temperature
Pail, Bag