KingRep EP10T®
Solvent free high strength epoxy paste.
Overview
KingRep EP10T is a two component, solvent-free, high strength adhesive and patching compound. Formulated to give an easily applied paste and suitable for sealant gun application, KingRep EP10T is thixotropic in nature and is suitable for vertical and overhead bonding and structural repairs. KingRep EP10T adheres well to most building materials without the need for a primer and will bond and cure under damp conditions, as well as exhibiting very good abrasion and chemical resistance along with negligible shrinkage.
Applications
- KingRep EP10T applications include:
- Patching repair to defective concrete
- Bonding concrete to concrete and metal to concrete
- For gap filling and pin holes in concrete
Technical Properties
| Property | Value | Standard |
|---|---|---|
| Appearance | Thick grey paste | — |
| Compressive strength | BS: > 30 MPa @ 1 day > 40 | — |
| 6319, Part 2 | 1983: MPa @ 3 days > 55 MPa @ 7 days | — |
| Tensile strength | ,: ≥ 10 MPa @ 20ºC @ 7 | BS 6319 |
| Part 7 | 1985: days | — |
| Flexural strength | EN: ≥ 20 MPa @ 20ºC @ 7 | — |
| 13892-2 | days | — |
| Bond strength | : > 2.0 @ 20ºC @ 7 days (concrete failure) | EN 1542 |
| Mixed density | 1.6 ± 0.1 g/cm3 | — |
| Working time | 60 - 90 min @ 25⁰C 25 - 45 min @ 35⁰C | — |
| Initial curing time | 24 hrs @ 25⁰C | — |
| VOC | < 20 g/ltr | — |
Standards & Approvals
Usage & Packaging
KingRep EP10T is available in 1 and 5 kg packs. KingRep EP10T can be applied up to 10 mm thickness per single layer at normal conditions.
1 kg Pack - 0.6 litre.
Shelf life is 1 year when stored under cover, out of direct sunlight and protected from extremes of temperature
Can
Product family
Crack filling polymer modified cementitious fairing coat repair mortar.
Shrinkage compensated free flowing micro concrete.
Medium build, high strength cementitious repair mortar.
One component medium build cementitious repair mortar.